| 1. | With the holding temperature going up , the globalization velocity accelerated gradually
随着保温温度的升高，获得半固态球状组织所需的等温时间逐步缩短。
|
| 2. | The semi - solid recrystallization velocity was run - up when the holding temperature risen and the heating velocity accelerated . 5
保温温度升高和连续加热速度加诀都会使半固态再结晶的速度提高。
|
| 3. | The relationship between the holding temperature and the average of the equal - area - circle diameter or the average of the roundness was parabolic
而等温温度对最终球化组织的平均等积圆直径和平均球化度的影响呈抛物线关系。
|
| 4. | When the preformed magnesium alloy ' s texture was globalizing , there were two important control factors , which were holding temperature and holding time , affecting the globalization processing
研究结果表明： 1 、等温温度和保温时间是形变镁合金组织球状化的两个重要控制因素。
|
| 5. | Ill 2 , xi ' an university of technology 2 . at the same holding temperature , when the holding time increased , the equal - area - circle diameter trended to uniform , and the distribution of the roundness approached to gaussian distribution
2 、相同等温温度条件下，改变等温时间，等积圆直径的分布随时间的延长趋向均匀，晶粒球化度接近于正态分布。
|
| 6. | 3 . at the same holding time , when the holding temperature changed , the number of the long equal - area - circle diameter grain increased , and the average of the equal - area - circle diameter lengthened , the average of the roundness heightened
3 、相同保温时间条件下，改变等温温度，等积圆直径大的晶粒随温度的升高而增加，球状化程度高的晶粒数增多，平均等积圆直径和平均球化度同时增大。
|
| 7. | Through ascension to another biochemistry that was present pre - atlantis when the equator held temperatures to this degree , then one quite naturally resonates and as such does not burn up , but feels quite comfortable as one ' s body temperature matches the temperature upon the land
藉由提升到早于亚特兰蒂斯的另一个生化体中? ?那时赤道就持有这么高的温度，你就能很自然地共振而并不灼烧，并且还感觉非常舒适，因为你的体温与大地的温度相吻合。
|
| 8. | There was a critical temperature tm between 1200 ~ 1215 . above the tm the relationship between the temperature and the extent of reaction of cu2o and al , which would react completely by keeping the time of holding temperature longer or rising temperature higher , is of liner relation . 3
Cu _ 2o与al的反应存在一个临界温度，这个临界温度为1200 1215之间的某一温度t _ m ，高于t _ m ，熔液温度的提高与cu _ 2o与al的反应进行的程度呈线性关系，并且延长保温时间或者继续升高反应温度最终都能使反应完全。
|
| 9. | Aimed at the high temperature at furnace roof and wall , great lost of body heat radiation , poor leading heating ability and long soaking time , the compound ceramic fiber coating is used to hold temperature of furnace roof and wall , make the heating loss dropped , shorten soaking time , improve heating ability and reduce evergy consumption
摘要针对环形炉炉顶炉墙表面温度高、炉体散热损失大、导致加热能力低、待温时间偏长的问题，选用了复合陶瓷纤维保温涂料，使炉体散热损失减少，待温时间缩短，加热能力提高，且能耗降低。
|